Siegenite

Siegenite
Siegenite from Buick mine, Bixby, Viburnum Trend District, Iron County, Missouri, USA
General
Category	Sulfide mineral Thiospinel group Spinel structural group
Formula (repeating unit)	(Ni,Co)3S4
IMA symbol	Seg[1]
Strunz classification	2.DA.05
Crystal system	Cubic
Crystal class	m3m
Space group	Fd3m (#227)
Unit cell	a = 9.33 Å; V = 810.94Å3
Identification
Formula mass	304.3 - 305 g/mol
Color	Light to steel-grey, violet-gray (tarnished)
Crystal habit	As octahedral crystals, granular, massive
Twinning	On {111}; polysynthetic
Cleavage	Imperfect on {001}
Fracture	Irregular to uneven, sub-conchoidal
Mohs scale hardness	4.5 - 5.5
Luster	Metallic
Streak	Grayish black
Diaphaneity	Opaque
Density	4.5 - 4.8 g/cm3 (Measured) 4.83 g/cm3 (Calculated)
References	[2][3][4]

Siegenite (also called grimmite, or nickel cobalt sulfide) is a ternary transition metal dichalcogenide compound with the chemical formula (Ni,Co)₃S₄. It has been actively studied as a promising material system for electrodes in electrochemical energy applications due to its better conductivity, greater mechanical and thermal stability, and higher performance compared to metal oxides currently in use.^[5] Potential applications of this material system include supercapacitors, batteries, electrocatalysis, dye-sensitized solar cells, photocatalysis, glucose sensors, and microwave absorption.^[6]

In synthetic chemistry, a range of chemical compositions with the formula Ni_xCo_3-xS₄ (0 < x < 3) are often referred to as the siegenite system. However, according to the new IMA list of minerals (updated November 2022), the normal spinel NiCo₂S₄ is called grimmite, the inverse spinel CoNi₂S₄ is called siegenite, and the endmembers Ni²⁺(Ni³⁺)₂S₄ and Co²⁺(Co³⁺)₂S₄ are called polydymite and linnaeite, respectively.^[7] In 2020, NiCo₂S₄ (grimmite) is approved as a valid mineral species by the IMA.^[8]

Siegenite was first described in 1850 for an occurrence in the Stahlberg Mine in Müsen, Siegerland, North Rhine-Westphalia, Germany and named for the locality.^[2] It occurs in hydrothermal copper-nickel-iron sulfide bearing veins associated with chalcopyrite, pyrrhotite, galena, sphalerite, pyrite, millerite, gersdorffite and ullmannite.^[3]

It occurs in a variety of deposits worldwide, including Brestovsko in the central Bosnian Mountains of Serbia; at Kladno in the Czech Republic; Blackcraig, Kirkcudbrightshire, Scotland. In the United States occurrences include the Mine la Motte of Madison County and the Buick mine, Bixby, Iron County and in the Sweetwater mine of Reynolds County in the Lead Belt of Missouri. In Canada, it is known from the Langis mine, Cobalt-Gowganda area, Ontario. In Africa it occurs at Shinkolobwe, Katanga Province and Kilembe, Uganda. In Japan, it is reported from the Kamaishi mine, Iwate Prefecture, and the Yokozuru mine, north Kyushu. It also occurs at Kalgoorlie, Western Australia.^[3] It is found at the Browns deposit, Batchelor, Northern Territory, Australia.^[2]

Siegenite is a member of the thiospinel group, which belongs to the cubic space group ${\displaystyle Fd{\bar {3}}m}$ (#227) and has the Pearson symbol ${\displaystyle cF56}$. Similar to normal spinels, a normal thiospinel unit cell consists of eight FCC sub unit cells of two different types, where S^2- anions occupy all the FCC lattice points. The first type of sub unit cell has 2+ cations occupying 2 of the 8 tetrahedral sites and 3+ cations occupying 3/2 of the 4 octahedral sites. The second type of sub unit cell has only 3+ cations occupying 5/2 of the 4 octahedral sites. These two types of sub unit cells are alternatively stacked, forming a NaCl-type superstructure.

For a normal thiospinel (NiCo₂S₄), Ni²⁺ cations occupy 1/8 of the tetrahedral sites to form NiS₄ tetrahedra and Co³⁺ cations occupy 1/2 of the octahedral sites to form CoS₆ octahedra. Each tetrahedron shares corners with 12 neighboring octahedra, and each octahedron shares corners with 6 tetrahedra and edges with 6 octahedra. For an inverse thiospinel (CoNi₂S₄), Ni²⁺ occupy 1/8 of the octahedral sites and Co³⁺ occupy 1/4 of the tetrahedra sites and 1/4 of the octahedral sites. For a mixed/complex thiospinel, both metal ions occupy tetrahedral and octahedral sites and can be expressed as (A_xB_1-x)_Td[A_2-xB_x]_OhX₄ (0 < x < 1), where A and B are metal ions, x is the degree of inversion, and ${\displaystyle T_{d}}$ and ${\displaystyle O_{h}}$ denote the tetrahedral and octahedral sites, respectively.

The powder X-ray diffraction (XRD) pattern of siegenite exhibits strong diffraction signals between 20° and 60° 2θ angles. The lattice constant of siegenite is measured to be 9.319 Å based on the strongest reflection at around 32°, corresponding to lattice plane (311), which agrees with the calculated lattice constant of 9.325 Å.^[9][10]

Unlike many binary and ternary semiconductor oxides, NiCo₂S₄ exhibits metallic properties and high electrical conductivity, which makes it useful as an electrode material in energy storage devices. The resistivity of NiCo₂S₄ is ~10³ μΩ cm at room temperature and its temperature coefficient of resistivity is positive and stays constant between 40 K and 300 K, which is indicative of a metallic compound.^[9] NiCo₂S₄ also has a very low Seebeck coefficient of 5 μV K^–1 and a carrier density of 3.18 × 10²² cm⁻³ higher than that of silver.^[9]

Reported synthetic routes of nickel cobalt sulfide include hydrothermal^[11][12] and solvothermal^[13] reactions, solvent-free thermal decomposition of xanthates,^[14] SILAR method for thin films,^[15] and solution-phase organometallic synthesis.^[16] The hydrothermal reaction is the most widely used synthesis method to fabricate intricate nanostructures on highly porous substrates, yielding hierarchical structures that maximize redox-active surface areas and promote high-rate supercapacitive performance of Ni-Co-S-based electrodes.

(Ni,Co)₃S₄ is a promising electrode material for batteries and supercapacitors. Since the electronegativity of sulfur is lower than that of oxygen, (Ni,Co)₃S₄ has a more flexible lattice compared to its oxide counterpart, which allows easier electron and ion transport through the structure.^[17] Its high ionic conductivity can be attributed to the abundance of available cation sites in the thiospinel structure, and its high redox activity comes from the highly electrochemically active Ni²⁺/Ni³⁺ and Co²⁺/Co³⁺ redox couples. In literatures, nanoporous Ni-Co-S composite materials have been shown to have both high specific capacity in Li-based batteries and high capacitance in supercapacitors.^[6]

(Ni,Co)₃S₄ has been considered as an alternative electrocatalyst for HER and OER reactions because of its high conductivity and low cost. It is reported that a overpotential of 87 mV for HER and 251 mV for HER can be achieved using NiCo₂S₄-based electrode, showing good potential for water splitting applications.^[6]